Ortho+E thermoplastische Klebeverbindung

Versatile low-temperature orthosis material , suitable for most applications.

Colour: standard light beige.

Characteristics:

• maximum stretch
• maximum deformability
• average elasticity
• maximum memory
• minimal stiffness
• very good bond during dry processing
• fairly smooth surface, good cleaning afterwards
• light beige, becomes transparent at processing temperature 60° to 65°
• application: all body parts
• warming: in a warm water tank at 60 to 65° for 60 to 90 sec. Per plate.
  
  

We offer a range of low-temperature thermoplastics and associated accessories. The thermoplastics have easy and reliable handling and deformability.
The heating takes place in a warm water bath at 60 to 65°C for 60 to 90 seconds.
When the material is removed from the bath, the surface temperature drops quite quickly to 40°C, allowing the correct shape to be measured directly on the skin.

After a few minutes the material starts to harden.
When heated dry, a very good connection is possible.
The material is RX permeable.

Perforations:
- None: smooth plate with maximum support, perfect for cleaning
- Micro: ±13%, many small holes, for more strength: choose a thicker plate
- Mini: scattered holes 3.5% perforation, the sheet remains approximately the same strength
- Opti: ±20%, multiple holes, optimal ventilation

Thicknesses:
- 1.6 mm: small splints such as for fingers, the hand and for children
- 2.0 mm: small splints that require a little more strength
- 2.5 mm: often used for static and dynamic splints for the hand and wrist
- 3.2 mm: suitable for larger splints

EOTP16A|125 EOTP16B|125 EOTP20A|125 EOTP20B|125 EOTP25A|125